Passive Q-ihinduranya cyangwa ibyuma byuzuza ibyara ingufu za laser pulses zidakoresheje amashanyarazi ya opt-optique, bityo bikagabanya ingano yipaki kandi bikuraho amashanyarazi menshi.Co.Spinel nikintu gikomeye, gihamye kristu isukuye neza.Cobalt isimbuza byoroshye magnesium muri Spinel host idakeneye izindi ndishyi zishyurwa.Igice kinini cyo kwinjiza (3.5 × 10-19 cm2) cyemerera Q-guhinduranya Er: ikirahuri cya lazeri idafite interacavité yibanda kuri flash-itara na pompe ya diode.Kwishima cyane-kwinjizwa na leta bivamo itandukaniro rinini cyane rya Q-switch, ni ukuvuga igipimo cyambere (ikimenyetso gito) no kwuzura kwuzuye kurenza 10.
Ibiranga:
• Birakwiriye kuri lazeri 1540 nm
Igice cyo kwinjiza cyane
• Kwirengagiza kwishima kwa leta
• Ubwiza buhanitse
• Ikwirakwizwa rimwe Co.
Porogaramu:
• Amaso meza 1540 nm Er: laser ikirahure
• 1440 nm laser
• 1340 nm laser
• Ijisho ririnda laser urutonde
Imiti yimiti | Co2+: MgAl2O4 |
Imiterere ya Crystal | Cubic |
Ibipimo bya latike | 8.07Å |
Ubucucike | 3.62 g / cm3 |
Ingingo yo gushonga | 2105 ° C. |
Ironderero | n = 1.6948 @ 1.54 µm |
Ubushyuhe bwumuriro / (W · cm-1· K.-1@ 25 ° C) | 0.033W |
Ubushyuhe bwihariye / (J · g-1· K.-1) | 1.046 |
Kwagura Ubushyuhe / (10-6/ ° C @ 25 ° C) | 5.9 |
Gukomera (Mohs) | 8.2 |
Ikigereranyo cyo kuzimangana | 25dB |
Icyerekezo | [100] cyangwa [111] <± 0.5 ° |
Ubucucike bwiza | 0.1-0.9 |
Ibyangiritse | > 500 MW / cm2 |
Doping yibanze kuri Co.2+ | 0.01-0.3 atm% |
Coefficient ya Absorption | 0 ~ 7 cm-1 |
Uburebure bwakazi | 1200 - 1600 nm |
Kwambara | AR / AR @ 1540 , R <0.2%;AR / AR @ 1340 , R <0.2% |
Icyerekezo cyo kwihanganira | <0.5 ° |
Umubyimba / Diameter Tolerance | ± 0,05 mm |
Ubuso | <λ / 8 @ 632 nm |
Kugoreka Umuhengeri | <λ / 4 @ 632 nm |
Ubwiza bw'ubuso | 10/5 |
Bisa | 10〞 |
Perpendicular | 5ˊ |
Sobanura neza | > 90% |
Chamfer | <0.1 × 45 ° |
Ibipimo ntarengwa | Dia (3-15) × (3-50) mm |